The corrosion and tribocorrosion resistance of PEO composite coatings containing α-Al2O3 particles on 7075 Al alloy
2018
Abstract Plasma electrolytic oxidation (PEO) of 7075 Al alloy was carried out in silicate base electrolyte containing 200 nm diameter α-Al2O3 particles for producing composite coatings. The process was performed under a soft-sparking regime using a pulsed bipolar signal with several concentrations of α-Al2O3 particles. It was found that the incorporation of α-Al2O3 particles into the coating did not significantly alter the thickness and roughness of the coating. However, the α-Al2O3 particles were detected on surface of the composite coatings. Corrosion tests showed significant improvement in corrosion performance of the composite coatings due to the efficient pore blocking provided by α-Al…
Effects of pulse current mode on plasma electrolytic oxidation of 7075 Al in Na2WO4 containing solution: From unipolar to soft-sparking regime
2018
Abstract Plasma electrolytic oxidation coatings were produced on 7075 Al alloy in a silicate based solution containing sodium tungstate using unipolar, usual bipolar and soft-sparking bipolar pulsed current regimes. X-ray diffraction proved that the coatings contain gamma alumina and metallic tungsten. EDS results showed that the tungsten content decreases with increasing the negative half cycle. Scanning electron microscopy showed that the pancake and volcano-like were dominant morphologies for the coatings produced by the unipolar and bipolar current regimes, respectively. Under unipolar current regime, a band of large pores is observed at the metal/coating interface, while they became di…